FeSiAl (Super Sendust)
FeSiAl alloy powder is produced by the vacuum atomization process. It features ultra-low oxygen content, high sphericity, controllable particle size distribution, uniform microstructure, good powder flowability, high apparent density, easy formability, high mechanical strength, and better corrosion resistance and oxidation resistance than pure iron powder. Endowed with soft magnetic properties including high magnetic permeability, low coercivity and low loss, it exhibits excellent magnetic stability in the medium-to-high frequency range.
Key word:
fesi
Category:
Molding Choke Powders
+86 16673138845
Core Characteristics
- Uniform &stable chemical composition and low oxygen content
- Superior morphology& fluidity
- High permeability, low coercivity, low core loss
- Stable magnetic properties at high temperature
- Good process adaptability
Applications
Soft Magnetic Cores, Mold Chokes
Components
- New energy vehicle motors
- Charging pile inductors
- Integrated electromagnetic components, EMI shielding
Chemical Composition (wt%)
|
Element |
Si |
Al |
Others |
Fe |
|||
|
O |
C |
P |
S |
||||
|
Content (wt%) |
8.5 – 9.9 |
5.0 – 6.0 |
≤0.05 |
≤0.03 |
≤0.02 |
≤0.01 |
Bal |
Typical Properties
|
Properties |
App. Density (g/cm3) |
Tap Density (g/cm3) |
Flowability (s/50g) |
Laser Particle Size (µm) |
||
|
D10 |
D50 |
D90 |
||||
|
Scope |
2.8 – 3.2 |
3.6 – 4.0 |
≤35 |
15 - 22 |
30 – 40 |
60 - 75 |
|
Test Standard |
GB/T1479-2016 |
GB/T5162-2006 |
GB/T1482-2010 |
GB/T19077-2016 |
||