SUS316L

316L stainless steel alloy powder is an iron-based alloy powder containing Cr, Ni, Mo, and ultra-low C. The 316L stainless steel alloy powder prepared under atomization conditions has low oxygen content (typically≤ 500ppm), high sphericity, excellent flowability and apparent density, low porosity, high density, and excellent corrosion resistance, making it a core material in Metal Injection Molding field.

Key word:

Category:

Metal Injection Molding Powders

+86 16673138845

Product Inquiry

Key Characteristics

An austenitic stainless steel powder
High Purity and low oxygen content
Excellent corrosion resistance
Good sentered density
High precision adaptability

Industrial Applications

Aerospace, Automotive
Biomedical industry
Communications
3C electronics

Chemical Composition (wt%)

Element	Cr	Ni	Mo	Others					Fe
Element	Cr	Ni	Mo	O	C	P	Si	Mn	Fe
Content (wt%)	16.0-18.0	10.0-14.0	2.0-3.0	≤0.05	≤0.03	≤0.03	≤1.00	≤2.00	Bal

Typical Properties

PSD	App Density (g/cm³)	Tap Density (g/cm³)	Flowability (s/50g)	Laser Particle Size (µm)
PSD	App Density (g/cm³)	Tap Density (g/cm³)	Flowability (s/50g)	D10	D50	D90
D50: 11μm	≥4.4	≥4.8	-	2.9 - 4.5	10.0 - 12.0	18 - 24
D50: 12μm	≥4.4	≥4.8	-	3.5 - 5.6	11.5 - 13.7	21- 26

Feedstock performance parameter

Parameter	MFI (g/10min)	Sintered density (g/cm³)	Shrinkage (%)	Yield strength	Tensile strength	Elongation A10	Hardness
Feedstock	1000	7.90	1.167	170 MPa	520 MPa	55%	120HV10
Range	600-1400	7.85 - 7.95	1.162 - 1.168	-	-	-	-