SUS316L
316L stainless steel powder is widely used in the laser cladding / thermal spraying industries, especially in applications where repair of high-value components and surface strengthening of key parts are required. The high molybdenum content in 316L stainless steel gives it superior resistance to pitting and crevice corrosion in environments containing chloride ions and other corrosive agents.
Key word:
Category:
Laser Cladding Powders
+86 16673138845
Key Characteristics
- Good uniformity of chemical composition
- High Purity and low oxygen content
- Excellent sphericity and high flowability
- Controllable particle size distribution
- Inheriting the excellent matrix properties of 316L alloy
Applications
- Metal injection molding (MIM)
- 3D printing
- Laser cladding
- Thermal spraying
- Hot isostatic pressing (HIP)
- Brazing
Industrial Applications
- Aerospace
- Automotive, rail transit
- Petrochemical
- Mining & construction machinery, Tools and molds
- Turbine, energy & electricity
Chemical Composition (wt%)
|
Element |
Cr |
Ni |
Mo |
Others |
Fe |
||||
| O | C | P | Si | Mn | |||||
|
Content (wt%) |
16.0–18.0 |
10.0 -14.0 |
2.0 – 3.0 |
≤0.05 |
≤0.03 |
≤0.03 |
≤1.00 |
≤2.00 |
Bal |
Remark: Testing standard: GB/T14992-2010, excluding Oxygen in GB/T11170-2008.
Typical Properties
|
Properties |
App. Density (g/cm3) |
Tap Density (g/cm3) |
Flowability (s/50g) |
Laser Particle Size (µm) |
||
|
D10 |
D50 |
D90 |
||||
| 15 - 53µm | 4.5 – 5.5 |
5.8 – 6.8 |
≤25 |
16 - 25 |
30 - 36 | 50 - 58 |
| 45 -105µm | 4.5 – 4.8 | 5.8 – 6.6 | ≤25 | 44 - 60 | 65 - 91 | 100 - 130 |
| 53-150µm | 4.5 – 4.8 | 5.8 – 6.6 | ≤25 | 47 - 66 | 75 - 110 | 130 - 165 |
|
Testing Criteria |
GB/T1479-2011 |
GB/T5162-2006 |
GB/T1482-2010 |
GB/T13320-2009 |
||